Communities

Writing
Writing
Codidact Meta
Codidact Meta
The Great Outdoors
The Great Outdoors
Photography & Video
Photography & Video
Scientific Speculation
Scientific Speculation
Cooking
Cooking
Electrical Engineering
Electrical Engineering
Judaism
Judaism
Languages & Linguistics
Languages & Linguistics
Software Development
Software Development
Mathematics
Mathematics
Christianity
Christianity
Code Golf
Code Golf
Music
Music
Physics
Physics
Linux Systems
Linux Systems
Power Users
Power Users
Tabletop RPGs
Tabletop RPGs
Community Proposals
Community Proposals
tag:snake search within a tag
answers:0 unanswered questions
user:xxxx search by author id
score:0.5 posts with 0.5+ score
"snake oil" exact phrase
votes:4 posts with 4+ votes
created:<1w created < 1 week ago
post_type:xxxx type of post
Search help
Notifications
Mark all as read See all your notifications »
Q&A

Is there a particular type of lead-free solder that does not degrade soldering tips?

+2
−0

I have had my soldering iron tips degrading at ridiculous rates. Granted, they are not very expensive, but sometimes it takes less than 8 hours of soldering for them to degrade to the point where they are no longer usable. I use a soft sponge for cleaning, don't leave the iron on for prolonged times and coat it with tin when not using it.

I see that the market is moving to lead-free solder (which is what I am using) and it is getting more difficult to acquire leaded solder. Yes, I have read that there are no real advantages of lead-free solder over leaded solder, except for reducing the waste that goes into the landmass.

However, assuming there are children and pets in the house, it would make sense to not have a spool of lead laying around. Naturally, it should be put away, but nobody is perfect, and you may forget etc.

Hence the question: Are there certain types of lead-free solder to look for, that are easy on the soldering iron tips? If so, are there particular chemical compounds that allow this?

History
Why does this post require moderator attention?
You might want to add some details to your flag.
Why should this post be closed?

1 comment thread

General comments (3 comments)

2 answers

You are accessing this answer with a direct link, so it's being shown above all other answers regardless of its score. You can return to the normal view.

+3
−0

A different type of solder, other than using lead-based solder, is probably not going to help. There are two causes to your problem:

  1. Crappy tips.
  2. Higher temperature required due to lead-free solder.

You can fix the first by getting a good soldering tool.

Leaded solder will help with the second. You cite several reasons not to use leaded solder. The disposal issue is valid (although quite minor), but the remaining ones are not, and the use of lead-free solder may actually make things worse:

children and pets in the house, it would make sense to not have a spool of lead laying around

There are far more dangerous substances in your house than leaded solder. Pretty much any cleaning chemical is worse, not to mention medicines. Simple touching, unlike with some cleaners, isn't going to cause problems. Teaching the kids to keep their hands off your electronics stuff, and putting away the solder when not in use should really be good enough.

The big point you are missing is that the main danger of solder to humans is the vaporized flux, not the metal itself. This is made more dangerous with lead-free solder due to the high temperatures. Kids standing near you watching you solder are exposed to significantly more harm due to inhaling flux fumes, than they would be by handling leaded solder.


In what manner the higher required temperature affect the service life of the tip …?

Chemical reactions and diffusions speed up with temperature. In this case, the metal of the tip slowly "dissolves" into the molten solder. Different metals vary in this. Copper is actually quite susceptible, which is one reason solder bonds with copper so well. Good quality soldering tips are copper on the inside (for good thermal conductivity), but coated with a metal that doesn't diffuse into molten solder as well. Higher temperatures speed up all these processes.

History
Why does this post require moderator attention?
You might want to add some details to your flag.

1 comment thread

General comments (2 comments)
+1
−0

PCB's and components are expected to be used with the common SAC solder, there's little reason to use SnPb, IMO. I learned on SnPb. After a brief transition for RoHS to re-calibrate the "feel" of it, never went back. Once or twice an oddball situation needed low melting point, used SnBi (also toxic I believe).

Things to look at, many already discussed

  • Temperature... Need good temp control. Use "extra hot" only when needed. Design pcb with more thermal reliefs when possible to avoid this need. Also, IMO no need for tiny tips, just ends up needing to turn the heat up. I use 2.4mm for everything.
  • I think name-brand tips with quality plating are worth it.
  • Avoid any abrasive cleaning of the tip, that would wear away the plating. (but after tip plating is already gone, go to town)
  • I am suspicious of aggressive fluxes. I think the stuff on solder wick might be such. Would not want to leave that on there for too long. Simply displace with regular solder when done with it.
  • The water quality on the sponge may be another wildcard factor with corrosion.
  • Not sure how important it is to wipe off the slag(?) frequently, but I do it.